Note to users. If you're seeing this message, it means that your browser cannot find this page's style/presentation instructions -- or possibly that you are using a browser that does not support current Web standards. Find out more about why this message is appearing, and what you can do to make your experience of our site the best it can be.

Originally published in Science Express on 27 November 2008
Science 9 January 2009:
Vol. 323. no. 5911, pp. 231 - 234
DOI: 10.1126/science.1165995
Prev | Table of Contents | Next

Reports

Direct Measurement of Molecular Mobility in Actively Deformed Polymer Glasses

Hau-Nan Lee, Keewook Paeng, Stephen F. Swallen, M. D. Ediger

When sufficient force is applied to a glassy polymer, it begins to deform through movement of the polymer chains. We used an optical photobleaching technique to quantitatively measure changes in molecular mobility during the active deformation of a polymer glass [poly(methyl methacrylate)]. Segmental mobility increases by up to a factor of 1000 during uniaxial tensile creep. Although the Eyring model can describe the increase in mobility at low stress, it fails to describe mobility after flow onset. In this regime, mobility is strongly accelerated and the distribution of relaxation times narrows substantially, indicating a more homogeneous ensemble of local environments. At even larger stresses, in the strain-hardening regime, mobility decreases with increasing stress. Consistent with the view that stress-induced mobility allows plastic flow in polymer glasses, we observed a strong correlation between strain rate and segmental mobility during creep.

Department of Chemistry, University of Wisconsin–Madison, Madison, WI 53706, USA.

Read the Full Text

To Advertise     Find Products

Science. ISSN 0036-8075 (print), 1095-9203 (online)