Note to users. If you're seeing this message, it means that your browser cannot find this page's style/presentation instructions -- or possibly that you are using a browser that does not support current Web standards. Find out more about why this message is appearing, and what you can do to make your experience of our site the best it can be.

Site Tools

  • AAAS
  • Subscribe
  • Feedback

Site Search

Search Advanced

Science 1 February 2008:
Vol. 319. no. 5863, pp. 600 - 604
DOI: 10.1126/science.1151205
Prev | Table of Contents | Next

Reports

Measuring the Surface Dynamics of Glassy Polymers

Z. Fakhraai and J. A. Forrest*

The motion of polymer chain segments cooled below the glass transition temperature slows markedly; with sufficient cooling, segmental motion becomes completely arrested. There is debate as to whether the chain segments near the free surface, or in thin films, are affected in the same way as the bulk material. By partially embedding and then removing gold nanospheres, we produced a high surface coverage of well-defined nanodeformations on a polystyrene surface; to probe the surface dynamics, we measured the time-dependent relaxation of these surface deformations as a function of temperature from 277 to 369 kelvin. Surface relaxation was observed at all temperatures, providing strong direct evidence for enhanced surface mobility relative to the bulk. The deviation from bulk {alpha} relaxation became more pronounced as the temperature was decreased below the bulk glass transition temperature. The temperature dependence of the relaxation time was much weaker than that of the bulk {alpha} relaxation of polystyrene, and the process exhibited no discernible temperature dependence between 277 and 307 kelvin.

Department of Physics and Astronomy and Guelph-Waterloo Physics Institute, University of Waterloo, Waterloo, Ontario N2L 3G1, Canada.